船用柴油机气阀阀面开裂的原因分析
蒋倩
0
南京国际船舶设备配件有限公司,江苏 南京 211121
摘要:针对所研究的船用柴油机气阀阀面开裂的问题,采用光学显微镜、电子显微镜、电子能谱仪和力学性能测试等方法对气阀阀面开裂原因进行试验和分析。结果表明:阀面堆焊合金存在缺陷是造成气阀阀面开裂的主要原因。并提出了改进建议。
关键词:  船用柴油机  阀面  开裂
Analysis on Causes of the Cracking of Marine Diesel Engine Valve Face
Jiang Qian
Nanjing International Marine Equipment & Spares Ltd., Jiangsu Nanjing 211121
Abstract:Aimed at the cracking of marine diesel engine valve face, light microscope, electron microscope, EDS and mechanical test were employed to carry out tests and analysis on the causes of the above mentioned fault. The results showed that the main cause is the defect of hardfacing alloys for the valve face. The improvement suggestions are thus put forward.
Key words:  marine diesel engine  valve face  cracking